    ISSN: 0449-2978
    Keywords: Physics ; Polymer and Materials Science
    Source: Wiley InterScience Backfile Collection 1832-2000
    Topics: Chemistry and Pharmacology , Physics
    Notes: Nylon 66 films exhibiting form I melting behavior show the γ mechanical relaxation at -140°C. Samples which have form II melting behavior do not show this relaxation. The γ relaxation disappears when material having form I behavior is converted to material having form II behavior by annealing or by cold drawing. The form I and form II types of melting behavior are also found in poly(ethylene terephthalate); the interconversions and thermal behavior of the forms are analogous to the nylon 66 case. In poly(ethylene terephthalate), the β relaxation at -40 to -60°C is present only when form I melting behavior is found. Conversion to form II melting behavior by annealing or drawing (80°C) again causes the relaxation to disappear. No β relaxation was found in amorphous polymer. The γ dispersion in nylon 66 and the β dispersion in poly(ethylene terephthalate) can therefore be associated with the crystalline structure responsible for form I melting behavior. Form I melting behavior has been associated with foldedchain crystals based on previous work. It is therefore postulated that the γ dispersion in nylon 66 and the β dispersion in poly(ethylene terephthalate) are associated with motions in the chain folds. This assignment is not inconsistent with the change in the γ dispersion of nylon 66 with the number of backbone CH2 units, since these will affect the fold structure.
    Additional Material: 10 Ill.