    Notes: X-ray photoelectron spectroscopy (XPS) was used to study the initial stages of surface oxidation of pseudomorphic Ni monolayers on Cu(111). Oxygen was adsorbed at 150 K followed by annealing the sample to 300 K and 600 K, respectively. For oxygen coverages between 0.4 ML and 2.0 ML we find little change in the peak shapes of the O 1s XPS signal. The Ni 2p3/2 spectra change, however, drastically: the onset of the oxidation is marked by the appearance of a peak doublet shifted with respect to the peak of metallic Ni. Based on these spectra we find a minimum oxygen coverage of 0.7 ML necessary for the onset of oxidation. The oxidation is nearly complete after the adsorption of about 2.0 ML oxygen. The exposure of different Ni coverages (0.5–2.0 ML) to oxygen shows that oxidation takes place only in the top-most Ni layer. © 2001 American Institute of Physics.
    Type of Medium: Electronic Resource
    Signatur Availability
    BibTip Others were also interested in ...
Close ⊗
This website uses cookies and the analysis tool Matomo. More information can be found here...